Archives

CSM fabrics for PPE

Our Range of CSM fabrics for Personal Protection Equipment.

ORCA® fabrics for PPE has been developed by our engineers to show the best resistances to
chemicals & hydrocarbons, 
abrasion, 
extreme temperatures,
with high flexibility.  

Each formulation of CSM compound is different to better reach the required properties.

ORCA TECH 295441 CSM Orange FI
Orange
  • Base fabric : Polyamide High Tenacity 235 dtex - 212 deniers
  • Coating : Chlorosulfonated Polyethylene (CSM)
  • Tensile strength : ≥ 127 daN/5cm (W)
  • Tear resistance : ≥ 1,7 daN
  • Surfacic mass : 570 (±50) g/m²
  • Permeation resistance to chemicals (EN 473-3) : H2SO4 96% L (Class 5), NaOH 40% K (Class 6), Methanol A (Class 5)
ORCA TECH 230155 CSM ALU SF
Aluminized
  • Base fabric : Meta Aramide
  • Coating : Chlorosulfonated Polyethylene (CSM) single side
  • Tensile strength : ≥ 170 daN/5cm (W)
  • Tear resistance : ≥ 8 daN (W)
  • Surfacic mass : 595 (±60) g/m²
  • Thermal Insulation (EN ISO 11612): Limited Spread Flame after 5 cycles washing (A1), Convective Heat (B2), Radiant Heat (C2), Aluminium Splashing (D3)
ORCA TECH 295497 CSM Military Grey FI
Military Grey
  • Base fabric : Polyamide High Tenacity 940 dtex
  • Coating : Chlorosulfonated Polyethylene (CSM)
  • Tensile strength : ≥ 285 daN/5cm
  • Peeling Test Adhesion : ≥ 10 daN
  • Surfacic mass : 955 (±100) g/m²

Orca Pennel & Flipo is certified

Quality, a shared philosophy

TPU BOOM

Orca Pennel & Flipo is certified

Quality, a shared philosophy

Double Side CSM-Coating

Our range of double side CSM fabrics for the industry.

ORCA® CSM fabrics show quite different properties, to adapt to each situation of your industry.

Mechanical properties can differ, the specific CSM compound guarantees you the following properties:

  • - UV resistant. 
  • - Abrasion.
  • - High and Low Temperature. 
  • - Strong fatigue resistant. 
  • - Hydrocarbure resistant. 

 

ORCA TECH 293405 35oz
Black FI
  • Base fabric : Polyamide High Tenacity 470 dtex - 425 deniers
  • Coating : Chlorosulfonated Polyethylene (CSM) double side
  • Tensile strength : ≥ 230 daN/5cm
  • Tear resistance : ≥ 5 daN
  • Surfacic mass : 1200 (±120) g/m²
  • This producted, used for dock shelter and machine protection, is particularly resistant to abrasion.
ORCA TECH 293402 35oz FR
Black FI
  • Base fabric : Polyamide High Tenacity 470 dtex - 425 deniers
  • Coating : Chlorosulfonated Polyethylene (CSM) double side
  • Tensile strength : ≥ 230 daN/5cm
  • Tear resistance : ≥ 5 daN
  • Surfacic mass : 1200 (±120) g/m²
  • This producted, is Flame Retardant formulated (FMVS302).
ORCA TECH 293xxx 16oz
Army Green FI
See all colors
  • Base fabric : Polyamide High Tenacity 470 dtex - 425 deniers
  • Coating : Chlorosulfonated Polyethylene (CSM) double side
  • Tensile strength : ≥ 230 daN/5cm
  • Tear resistance : ≥ 5 daN
  • Surfacic mass : 560 (±80) g/m²
  • This producted, designed for machine/ mining protection and military jackets, is available in various colors.
Ice White FI
Black FI
Yellow Colorado FI
Etna Red FI
Deer Brown FI
Alpin Blue FI
Artic Grey FI
Military Grey FI
Army Green FI
ORCA TECH 295443 Double Side CSM WHITE / NATO GREEN IR
White /NATO Green
See all colors
  • Base fabric : Polyamide High Tenacity 235 dtex - 212 deniers
  • Coating : Chlorosulfonated Polyethylene (CSM) double side
  • Tensile strength : ≥ 127 daN/5cm (W) // ≥ 98 daN/5cm (F)
  • Tear resistance : 1,7 daN
  • Surfacic mass : 550 (±100) g/m²
  • This fabric is bi-color: White internal side to offer the least heat onto the surface, NATO Green on the external side with Infra Red reflectance.
  • It has been engineered for military use, to offer stealth cover for helicopters and military vehicles.
IR NATO GREEN

Orca Pennel & Flipo is certified

Quality, a shared philosophy

Double Side CR-Coating

Our range of double side CR fabrics for the industry.

ORCA® CR fabrics show quite different properties, to adapt to each situation of your industry.  

These fabrics show a great ratio weight/ mechanical properties. The specific CR compound guarantees you the following properties: 

 
_ particularly strong abrasion resistance,
_ good UV and weather resistance,
_ strong adhesion onto the textile,
_ good chemical and hydrolysis resistance.

 

These characteristics allow these fabrics to be used in demanding mechanical and abrasion applications such as the manufacturing of lifting bags.

 

ORCA TECH 220176 0.8MM
Black
  • Base fabric : Polyamide High Tenacity
  • Coating : Polychloroprene (CR) double side
  • Tensile strength : ≥ 275 daN/5cm
  • Surfacic mass : 915 (±150) g/m²
ORCA TECH 220143 0.85MM
Black
  • Base fabric : Polyester High Tenacity 1670 dtex - 1500 deniers
  • Coating : Polychloroprene (CR) double side
  • Tensile strength : ≥ 420 daN/5cm
  • Tear resistance : ≥ 30 daN
  • Surfacic mass : 1015 (±150) g/m²
ORCA TECH 220144 1.2MM
Black
  • Base fabric : Polyamide High Tenacity 1880 dtex - 1690 deniers
  • Coating : Polychloroprene (CR) double side
  • Tensile strength : ≥ 520 daN/5cm
  • Tear resistance : ≥ 45 daN
  • Surfacic mass : 1400 (±200) g/m²
ORCA TECH 220145 1.45MM
Black
  • Base fabric : Polyamide High Tenacity 1880 dtex - 1690 deniers
  • Coating : Polychloroprene (CR) double side
  • Tensile strength : ≥ 800 daN/5cm (W) // ≥ 700 daN/5cm (F)
  • Tear resistance : ≥ 65 daN
  • Surfacic mass : 1650 (±200) g/m²
ORCA TECH 229613 ARAMIDE 1.15MM
Black
  • Base fabric : Polyaramide 1680 dtex - 1500 deniers
  • Coating : Polychloroprene (CR) double side
  • Tensile strength : ≥ 1000 daN/5cm
  • Surfacic mass : 1460 (±180) g/m²
ORCA TECH 220158 2MM
Black
  • Base fabric : Polyamide High Tenacity 1880 dtex - 1690 deniers
  • Coating : Polychloroprene (CR) double side
  • Tensile strength : ≥ 1100 daN/5cm
  • Surfacic mass : 2210 (±300) g/m²

Orca Pennel & Flipo is certified

Quality, a shared philosophy

CR BOOM

268 650 CR
Black
  • 1000 gsm
268 651 CR
Black
  • 1000 gsm
268 652 CR
Black
  • 1000 gsm

Orca Pennel & Flipo is certified

Quality, a shared philosophy

Uncured NR-SBR Sheets

Our ORCA® sheets are designed and tested to offer outstanding mechanical resistances to be used under extreme conditions (pressure, temperature and abrasion). 

These sheets has been developed to ensure best adhesion with uncured ORCA® fabrics when vulcanized by press, mould or autoclave, along with top ageing properties.

F.TECH uncured NR-SBR Sheet
Black
  • Uncured Sheet
  • Thicknesses (mm): 0,5 / 0,7 /1,1 / 1,2 / 1,3/  2,4

Orca Pennel & Flipo is certified

Quality, a shared philosophy

TECH VULC

201 299
Blue
  • CR
  • 1,2mm
  • Medical
239 596
  • NBR
  • 1mm
245 566
Black
  • CR
  • 0,7mm

Orca Pennel & Flipo is certified

Quality, a shared philosophy

UNCURED NBR/NPVC Sheets

Pennel & Flipo has developped a large range of uncured NBR/NPVC sheets, in several thicknesses, to be used in manufacturing products with uncured ORCA® fabrics.

These sheets has been developed to ensure best adhesion with uncured ORCA® fabrics when vulcanized by press or autoclave, along with top ageing properties.

F.TECH uncured NBR Sheet
Black
  • Uncured Sheet
  • thicknesses: 0.3mm - 0.6mm - 0.7mm - 1.2mm
F.TECH uncured NPVC Sheet
Black
See all colors
  • Uncured Sheet
  • thicknesses: 0.42mm - 0.5mm - 0.6mm - 0.7mm - 1mm - 1.2mm - 1.4mm - 3mm
  • Can be used for Flexible Oil Tanks.
NATO Green
Sand
Orange

Orca Pennel & Flipo is certified

Quality, a shared philosophy

ORCA® fabrics for RAFT

Check our range of TPU & CSM fabrics for Safety applications.

Our range of single side and double side TPU fabrics for Life Rafts are SOLAS certified, as well as single side CSM for Canopy.

ORCA® SAFETY fabrics for have been designed to show the best resistances to:

_ air & water tightness, 
_ low temperatures,
_ UV, 
_ mechanical properties, 
_ abrasion, 
_ with the lowest weight. 

ORCA® TPU fabrics are easily weldable (hot air, high frequency...) or glued. 

ORCA® 290 153
SF black
  • Base fabric : Polyamide High Tenacity 940 dtex
  • Coating : Polyurethane (TPU) single side
  • Tensile strength : ≥ 275 daN/5cm (W)
  • Tear resistance : ≥ 150 daN
  • Surfacic mass : 460 (±10%) g/m²
ORCA® 290 162
SF orange
  • Base fabric : Polyamide High Tenacity 940 dtex
  • Coating : Polyurethane (TPU) single side
  • Tensile strength : ≥ 275 daN/5cm (W)
  • Tear resistance : ≥ 150 daN
  • Surfacic mass : 460 (±10%) g/m²
ORCA® Tech 210 Textane
SF Yellow
See all colors
  • Base fabric : Polyamide High Tenacity 235 dtex
  • Coating : Poluyrethane (TPU) single side
  • Tensile strength : ≥ 93 daN/5cm (W)
  • Surfacic mass : 265 (±30) g/m²
Orange
Yellow
ORCA® 289 164
DF black
  • Base fabric : Polyamide High Tenacity 940 dtex
  • Coating : Polyurethane (TPU) double side
  • Tensile strength : ≥ 275 daN/5cm (W)
  • Tear resistance : ≥ 130 daN (W)
  • Surfacic mass : 710 (±50) g/m²
ORCA® 289 165
DF orange
  • Base fabric : Polyamide High Tenacity 940 dtex
  • Coating : Polyurethane (TPU) double side
  • Tensile strength : ≥ 275 daN/5cm (W)
  • Tear resistance : ≥ 130 daN (W)
  • Surfacic mass : 745 (±85) g/m²
ORCA® Tech A/2B 210 Textane
DF Orange
  • Base fabric : Polyamide High Tenacity 235 dtex
  • Coating : Poluyrethane (TPU) double side
  • Tensile strength : ≥ 110 daN/5cm (W)
  • Surfacic mass : 330 (±30) g/m²
ORCA® 255183 CANOPY
SF Orange
  • Base fabric : Polyamide High Tenacity 235 dtex
  • Coating : CSM polymer single side
  • Tensile strength : ≥ 110 daN/5cm (W)
  • Tear resistance : ≥ 50 daN
  • Surfacic mass : 179 (±14) g/m²

Orca Pennel & Flipo is certified

Quality, a shared philosophy

NR Engineered fabrics for Hovercrafts

Our range of NR fabrics for fingers.

ORCA® fabrics for Hovercraft has been developed by our engineers to show the best resistances to

 
_ abrasion,
_ low temperatures
_ and UV,
_ with high flexibility
_ and the lowest friction rate. 



 

Fingers materials require
high level of abrasion resistance,
high level of flogging resistance,
high range of temperature resistance
and low friction rate. 



 

With very low friction rate, Natural Rubber is the best compound to combine these properties.

ORCA TECH 220126 PA600 DF NR 1MM
Black
  • Base fabric : Polyamide High Tenacity 940 dtex - 846 deniers
  • Coating : Natural Rubber (NR) double side
  • Tensile strength : ≥ 450 daN/5cm
  • Tear resistance : ≥ 35 daN (W) // ≥ 30 daN (F)
  • Surfacic mass : 1025 (±100) g/m²
ORCA TECH 120898 PA600 DF NR 1.2MM
Black
  • Base fabric : Polyamide High Tenacity 940 dtex - 846 deniers
  • Coating : Natural Rubber (NR) double side
  • Tensile strength : ≥ 450 daN/5cm
  • Peeling test adhesion : ≥ 45 daN/5cm
  • Surfacic mass : 1285 (±150) g/m²
ORCA TECH 120881 PA600 DF NR 1.65MM
Black
  • Base fabric : Polyamide High Tenacity 940 dtex - 846 deniers
  • Coating : Natural Rubber (NR) double side
  • Tensile strength : ≥ 550 daN/5cm
  • Tear resistance : ≥ 28 daN
  • Surfacic mass : 1700 (±10%) g/m²
ORCA TECH 120867 PA800 DF NR 2.8MM
Black
  • Base fabric : Polyamide High Tenacity 1880 dtex - 1694 deniers
  • Coating : Natural Rubber (NR) double side
  • Tensile strength : ≥ 850 daN/5cm (W) // ≥ 750 daN/5cm (F)
  • Tear resistance : ≥ 130 daN
  • Surfacic mass : 2900 (±10%) g/m²